The negative electrode material with high capacity density and cycle performance produced by optimizing artificial graphite precursor, shaping coating and improving capacity density is widely used in 3C and power battery fields.
| Name | Model | D50 (μm) | Vibration compaction (g/cm3) | Comparison table (m2/g) | Pole piece compaction (g/cm3) | Capacity (mAh/g) | First effect (%) | characteristic | purpose |
| Cost effective artificial graphite | E1 | 15.1 | 1.15 | 1.43 | 1.50-1.60 | 346.5 | 92.7 | Excellent comprehensive performance and high cost performance | Power, square, energy storage battery |
| E15 | 15.5 | 1.21 | 1.28 | 1.60-1.70 | 353.9 | 92.9 | E1 capacity enhancement, higher cost performance | ||
| High rate artificial graphite | E12 | 9.3 | 1.10 | 1.95 | 1.45-1.55 | 345.0 | 92.5 | High magnification | Aircraft model, UAV, plant protection machine battery |
| E6 | 9.0 | 1.04 | 1.47 | 1.45-1.55 | 343.5 | 92.0 | High rate, low temperature and fast charging | ||
| E6-C | 7.2 | 1.08 | 1.82 | 1.40-1.50 | 342.4 | 92.2 | Low temperature and fast charging | UAV, start stop power supply, low temperature battery | |
High capacity density artificial graphite | E5-D | 14.1 | 1.11 | 1.41 | 1.70-1.80 | 358.6 | 93.3 | High density | 3C products, cylindrical batteries |
| E5-F | 14.6 | 1.13 | 1.49 | 1.70-1.80 | 356.1 | 93.5 | Higher capacity density and faster charging | ||
Low temperature quick filling artificial graphite | E9 | 9.7 | 1.08 | 1.39 | 1.50-1.60 | 353.2 | 92.1 | High capacity density and low temperature fast charging | Low temperature battery, electronic cigarette, power fast charging |
| E9-F | 13.2 | 1.10 | 1.05 | 1.55-1.65 | 352.0 | 91.8 | High capacity density, low temperature and fast charging | Low temperature battery, high-end electronic cigarette, power fast charging | |
| E9-D | 16.4 | 1.07 | 0.84 | 1.70-1.80 | 357.2 | 92 | High capacity density and low temperature fast charging | Digital fast charging, high-end electronic cigarette |